SMC不饱合树脂层压板

品 名

Grade

WS-GPO-3

适用标准

JIS

TL-GEF

NEMA

GPO-3

材质

Base and resin

不饱合聚脂树脂

Unsaturated polyester resin

试验项目

Testing item

单位

Unit

处理条件

Processing

Condition

短切玻璃纤维毡

Chopped stand mad

平行层向耐电压

Flatwise –with stand voltage

kv/mm

C-90/20/65

10

垂直层向耐电压

Edgewise-withstand voltage

kv

O-0.5/90

10

绝缘电阻

Insulation

resistance

常态

Normal condition

MΩ

C-90/20/65

10⁵-10⁷

煮沸后

After boiling

MΩ

C-90/20/65

+D-2/100

10¹-10²

体积电阻系数

Volume resistivity

MΩ-cm

C-90/20/65

10⁶-10⁸

表面电阻系数

Surface resistivity

MΩ

C-90/20/65

10⁵-10⁷

介电常数(1MHz)

Dielectric constant

―

C-90/20/65

4．5-5．0

介电损耗 (1MHz)

Dielectric loss tangent

―

C-

90/20/65

0．020-0．030

耐电弧性

Arc resistance

sec

A

180-190

耐电磨性

Tracking resistance

V(CTI)

A

550-600

弯曲强度

Flexural strength

垂直层向

Perpendicular to laminae

MP

A

180-230

压缩强度

Compressive

strength

垂直层向

Perpendicular to laminae

MPa

A

290-390

平行层向

Parallel to laminae

MPa

A

150-250

拉伸强度

Tensile strength

MPa

A

100-200

杨氏模量

Young’s modulus

MPa

A

12740-15680

粘结强度

Bonding strength

kN

A

5．0-6．5

洛氏硬度测量

Rockwell hardness

HR-R

A

115-120

埃左氏冲击强度

Izod impact strength

平行层向

Parallel to laminae

J/cm

A

3．4-4．4

加热后外观

Appearance after heating

℃/2hr

A

150

吸水率 (厚 1.0mm)

Water absorption(Thickness 1.0mm)

％

E -24/50

+D-24/23

0．20-0．40

比重

Specific gravity

―

A

1．95-2．05

热膨胀系数

Thermal

expansion

垂直层向

Perpendicular to laminae

1/℃

RT~ 200℃

1．2×10^-4

平行层向

Parallel to laminae

1/℃

RT~ 200℃

9．6×10^-6

耐燃性

Burning

resistance

UL-94法

―

C-48/23/50

&E-168/70

UL-94V-0

铁路车辆燃烧试验

Burning quality test for rolling stock

―

A

难燃性